Semiconductor device and fabrication method thereof

ABSTRACT

A semiconductor device includes a gate stack, an isolation structure and a strained feature. The gate stack is over a substrate. The isolation structure is in the substrate. The strained feature is disposed between the gate stack and the isolation structure and disposed in the substrate. The strained feature includes an upper surface adjacent to the isolation structure having a first crystal plane and a sidewall surface adjacent to the gate stack having a second crystal plane. The first crystal plane is different from the second crystal plane.

PRIORITY CLAIM

The present application is a divisional of U.S. application Ser. No. 13/252,346, filed Oct. 4, 2011, which is incorporated herein by reference in its entirety.

FIELD

The disclosure relates to integrated circuit fabrication and. more particularly. to a semiconductor device with a strained structure.

BACKGROUND

When a semiconductor device, such as a metal-oxide-semiconductor field-effect transistor (MOSFET), is scaled down through various technology nodes, high-k gate dielectric layers and metal gate electrode layers are incorporated into the gate stack of the MOSFET to improve device performance with the decreased feature sizes. In addition, strained structures in source and drain (S/D) recess cavities of the MOSFET utilizing selectively grown silicon germanium (SiGe) may be used to enhance carrier mobility.

However, there are challenges to implement such features and processes in complementary metal-oxide-semiconductor (CMOS) fabrication. As the gate length and spacing between devices decrease, these problems are exacerbated. For example, it is difficult to achieve enhanced carrier mobility for a semiconductor device, because strained materials cannot deliver a given amount of strain into the channel region of the semiconductor device, thereby increasing the likelihood of device instability and/or device failure.

BRIEF DESCRIPTION OF THE DRAWINGS

The present disclosure is best understood from the following detailed description when read with the accompanying figures. It is emphasized that, in accordance with the standard practice in the industry, various features are not drawn to scale and are used for illustration purposes only. In fact, the relative dimensions of the various features may be arbitrarily increased or reduced for clarity of discussion.

FIG. 1 is a flowchart illustrating a method for fabricating a semiconductor device comprising a strained structure according to various aspects of the present disclosure; and

FIGS. 2-8 show schematic cross-sectional views of a strained structure of a semiconductor device at various stages of fabrication according to various aspects of the present disclosure.

DESCRIPTION

It is understood that the following disclosure provides many different embodiments, or examples, for implementing different features of the disclosure. Specific examples of components and arrangements are described below to simplify the present disclosure. These are, of course, merely examples and are not intended to be limiting. For example, the formation of a first feature over or on a second feature in the description that follows may include embodiments in which the first and second features are formed in direct contact, and may also include embodiments in which additional features may be formed between the first and second features, such that the first and second features may not be in direct contact. In addition, the present disclosure may repeat reference numerals and/or letters in the various examples. This repetition is for the purpose of simplicity and clarity and does not in itself dictate a relationship between the various embodiments and/or configurations discussed.

FIG. 1 is a flowchart illustrating a method 100 for fabricating a semiconductor device 200 according to various aspects of the present disclosure. FIGS. 2-8 show schematic cross-sectional views of a semiconductor device 200 at various stages of fabrication according to an embodiment of the method 100 of FIG. 1. The semiconductor device 200 may be included in a microprocessor, memory cell, and/or other integrated circuit (IC). It is noted that the method of FIG. 1 does not produce a completed semiconductor device 200. A completed semiconductor device 200 may be fabricated using complementary metal-oxide-semiconductor (CMOS) technology processing. Accordingly, it is understood that additional processes may be provided before, during, and after the method 100 of FIG. 1, and that some other processes may only be briefly described herein. Also, FIGS. 1 through 8 are simplified for a better understanding of the present disclosure. For example, although the figures illustrate the semiconductor device 200, it is understood the IC may comprise a number of other devices comprising resistors, capacitors, inductors, fuses, etc.

Referring to FIGS. 1 and 2, the method 100 begins at step 102 wherein a substrate 202 comprising a surface 202 s is provided. In one embodiment, the substrate 202 comprises a crystalline silicon substrate (e.g., wafer). In the present embodiment, the substrate 202 is referred to as a (100) substrate having the surface 202 s formed of the (100) crystal plane. In an alternative embodiment, the substrate 202 may include a silicon-on-insulator (SOI) structure.

The substrate 202 may further comprise active regions 204. The active regions 204 may include various doping configurations depending on design requirements. In some embodiments, the active regions 204 may be doped with p-type or n-type dopants. For example, the active regions 204 may be doped with p-type dopants, using a chemical such as boron or BF₂ to perform the doping; n-type dopants, using a chemical such as phosphorus or arsenic to perform the doping; and/or combinations thereof. The active regions 204 may act as regions configured for a N-type metal-oxide-semiconductor transistor device (referred to as an NMOS) and regions configured for a P-type metal-oxide-semiconductor transistor device (referred to as a PMOS).

In some embodiments, isolation structures 206 a and 206 b are formed in the substrate 202 to isolate the various active regions 204. The isolation structures 206 a and 206 b, for example, are formed using isolation technology, such as local oxidation of silicon (LOCOS) or shallow trench isolation (STI), to define and electrically isolate the various active regions 204. In the present embodiment, the isolation structures 206 a and 206 b include a STI. The isolation structures 206 a and 206 b may comprise silicon oxide, silicon nitride, silicon oxynitride, fluoride-doped silicate glass (FSG), a low-K dielectric material, other suitable materials, and/or combinations thereof. The isolation structures 206 a and 206 b, and in the present embodiment the STI, may be formed by any suitable process. As one example, the formation of the STI may include patterning the semiconductor substrate 202 by a photolithography process, etching a trench in the substrate 202 (for example, by using a dry etching, wet etching, and/or plasma etching process), and filling the trench (for example, by using a chemical vapor deposition process) with a dielectric material. In some embodiments, the filled trench may have a multi-layer structure such as a thermal oxide liner layer filled with silicon nitride or silicon oxide.

Still referring to FIG. 2, in at least one embodiment, gate stacks 210 a, 210 b, and 210 c are formed over the surface 202 s of the substrate 202. In some embodiments, the gate stacks 210 a, 210 b, and 210 c are formed by sequentially depositing and patterning a gate dielectric layer 212, a gate electrode layer 214, and a hard mask layer 216 on the substrate 202.

The gate dielectric layer 212, in one example, is a thin film comprising silicon oxide, silicon nitride, silicon oxynitride, high-k dielectrics, other suitable dielectric materials, or combinations thereof. High-k dielectrics comprise metal oxides. Examples of metal oxides used for high-k dielectrics include oxides of Li, Be, Mg, Ca, Sr, Sc, Y, Zr, Hf, Al, La, Ce, Pr, Nd, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm, Yb, Lu and mixtures thereof. In the present embodiment, the gate dielectric layer 212 is a high-k dielectric layer with a thickness in the range of about 10 angstroms to about 30 angstroms. The gate dielectric layer 212 may be formed using a suitable process such as atomic layer deposition (ALD), chemical vapor deposition (CVD), physical vapor deposition (PVD), thermal oxidation, UV-ozone oxidation, or combinations thereof. The gate dielectric layer 212 may further comprise an interfacial layer (not shown) to reduce damage between the gate dielectric layer 212 and substrate 202. The interfacial layer may comprise silicon oxide.

The gate electrode layer 214 is then formed on the gate dielectric layer 212. In some embodiments, the gate electrode layer 214 may comprise a single layer or multilayer structure. In the present embodiment, the gate electrode layer 214 may comprise polysilicon. Further, the gate electrode layer 214 may be doped polysilicon with the same or different doping species. In one embodiment, the gate electrode layer 214 has a thickness in the range of about 30 nm to about 60 nm. The gate electrode layer 214 may be formed using a process such as low-pressure chemical vapor deposition (LPCVD), plasma enhanced chemical vapor deposition (PECVD), other suitable processes, or combinations thereof.

Next, the hard mask layer 216 is formed over the gate electrode layer 214 and a patterned photo-sensitive layer (not shown) is formed on the hard mask layer 216. The pattern of the photo-sensitive layer is transferred to the hard mask layer 216 and then transferred to the gate electrode layer 214 and gate dielectric layer 212 to form the gate stacks 210 a, 210 b, and 210 c over the surface 202 s of the substrate 202. In some embodiments, the hard mask layer 216 comprises silicon oxide. Alternatively, the hard mask layer 216 may comprise silicon nitride, silicon oxynitride, and/or other suitable dielectric materials, and may be formed using a method such as CVD or PVD. The hard mask layer 216 has a thickness in the range from about 100 angstroms to about 800 angstroms. The photo-sensitive layer is stripped thereafter by a dry and/or wet stripping process.

Referring to FIGS. 1 and 3, the method 100 proceeds to step 104 wherein gate spacers 218 are formed overlying opposite sidewalls of the gate stacks 210 a, 210 b, and 210 c. In the present embodiment, the gate spacers 218 adjoin sidewalls of the gate stacks 210 a, 210 b. In some embodiments, the gate spacers 218 may include a single-layer or a multiple-layer structure. In the present embodiment, a blanket layer of spacer material (not shown) is formed over the gate stacks 210 a, 210 b, and 210 c by a deposition process including CVD, PVD, ALD, or other suitable techniques. In some embodiments, the spacer material comprises silicon oxide, silicon nitride, silicon oxynitride, other suitable material, or combinations thereof. In some embodiments, the spacer material has a thickness ranging from about 5 nm to about 15 nm. Then, an anisotropic etching is performed on the spacer material to form the gate spacers 218.

Referring to FIGS. 1 and 4, the method 100 continues with step 106 in which the substrate 202 is recessed to form recess cavities 220, 230, 240, and 250 in the substrate 202. In some embodiments, the recess cavities 220, 230, 240, and 250 are source and drain (S/D) recess cavities. In the structure of FIG. 4, the recess cavities 220 and 250 are formed between the gate stack 210 a/the isolation structure 206 a and the gate stack 210 c/the isolation structure 206 b, respectively. The recess cavities 230 and 240 are formed between the gate stacks 210 a/210 b and 210 b/210 c, respectively.

In the present embodiment, the processes for forming the recess cavities 220, 230, 240, and 250 are started using an isotropic dry etching process, followed by an anisotropic wet or dry etching process. In some embodiments, the isotropic dry etching process is performed using the gate spacers 218 and isolation structures 206 a and 206 b as hard masks to recess the surface 202 s of the substrate 202 that is unprotected by the gate spacers 218 or the isolation structures 206 a and 206 b to form initial recess cavities (not shown) in the substrate 202. In an embodiment, the isotropic dry etching process may be performed under a pressure of about 1 mTorr to about 1000 mTorr, a power of about 50 W to about 1000 W, a bias voltage of about 20 V to about 500 V, at a temperature of about 40° C. to about 60° C., using HBr and/or Cl₂ as etch gases. Also, in the embodiments provided, the bias voltage used in the isotropic dry etching process may be tuned to allow better control of an etching direction to achieve desired profiles for the S/D recess regions.

In some embodiments, a wet etching process is then provided to enlarge the initial recess cavities to form the recess cavities 220, 230, 240, and 250. In some embodiments, the wet etching process is performed using a chemical comprising hydration tetramethyl ammonium (TMAH), or the like. As a result of such etching processes, there may be formed a plurality of facets in each recess cavities 220, 230, 240, and 250. It should be noted that periphery environment with or without an etch stop can influence resultant features of the S/D recess cavities 220, 230, 240, and 250. During the wet etching process, the isolation structure 206 a may function as an etch stop for defining the recess cavity 220 between the gate stack 210 a and isolation structure 206 a. In some embodiments, the recess cavity 220 between the gate stack 210 a and isolation structure 206 a have respective sidewall surfaces defined by a bottom facet 220 c, an upper sidewall facet 220 a, lower sidewall facets 220 b and 220 d, and an upper portion of the sidewall of the isolation structure 206 a. Thereby, the facet 220 a and facet 220 b thus formed intersect each other and together define a wedge 220 w in the recess cavity 220, such that the wedge-shaped recess cavity 220 extends into the substrate 202 in the region right underneath the spacer 218 toward the channel region. In some embodiments, the recess cavity 230 between the adjacent gate stacks 210 a and 210 b, without an etch stop, have respective sidewall surfaces each defined by a bottom facet 230 c, upper sidewall facets 230 a, 230 e, and lower sidewall facets 230 b and 230 d. Thereby, the facet 230 d and facet 230 e thus formed intersect each other and together define a wedge 230 w in the recess cavity 230, such that the wedge-shaped recess cavity 230 extends into the substrate 202 in the region right underneath the spacer 218 toward the channel region.

In the illustrated example, the bottom facets 220 c, 230 c are formed of (100) crystal plane parallel to the crystal plane of the surface 202 s of the substrate 202. In the illustrated example, the upper sidewall facets 220 a, 230 a, and 230 e and the lower sidewall facets 220 b, 220 d, 230 b, and 230 d are formed of (111) crystal plane, and the upper sidewall facets 220 a and 230 a form an angle θ₁ to the bottom facets 220 c and 230 c. Further, the lower sidewall facets 220 b and 230 b form a smaller angle θ₂ than the angle θ₁ with respect to the bottom facets 220 c and 230 c. In the structure of FIG. 4, the angle θ₁ takes the range of about 90 degrees to about 150 degrees, while the angle θ₂ takes the range of about 40 degrees to about 60 degrees. In the present embodiment, the angles θ₁, θ₂ take the values of about 146 degrees and about 56 degrees, respectively in the case the facets 220 a, 230 a, 220 b, and 230 b are formed by the (111) crystal plane of the substrate 202. However, it should be noted that the structure of FIG. 4 is not limited to the case in which the facets 220 a, 230 a, 220 b, and 230 b are formed by the (111) crystal plane.

Further, the bottom facet 220 c is formed at a depth D₁ as measured from the surface 202 s of the substrate 202, while the upper facet 220 a is formed down to a depth D₂. In the structure of FIG. 4, the depth D₁ is in the range of about 20 nm to about 70 nm, while the depth D₂ is in the range of about 5 nm to about 60 nm. By optimizing the depth D₂ and a distance between the mutually opposing wedges 220 w, 230 w, it becomes possible to confine the uni-axial compressive stress of a strained material 222 (shown in FIG. 5) effectively to the channel region, thereby enhancing the device performance.

The process steps up to this point have provided the substrate 202 having the recess cavities 220, 230, 240, 250 adjacent to the gate stacks 210 a, 210 b, and 210 c. Referring to FIGS. 1 and 5, the method 100 continues with step 108 in which a strained material 222 is grown in the recess cavities 220, 230, 240, 250 of the substrate 202 using a process including selective epitaxy growth (SEG), cyclic deposition and etching (CDE), chemical vapor deposition (CVD) techniques (e.g., vapor-phase epitaxy (VPE) and/or ultra-high vacuum CVD (UHV-CVD)), molecular beam epitaxy (MBE), other suitable epi processes, or combinations thereof. In some embodiments, the strained material 222 has a lattice constant different from the substrate 202 to induce a strain or stress on the channel region of the semiconductor device 200, and therefore enable carrier mobility of the device to enhance the device performance.

In the present embodiment, a pre-cleaning process is performed to clean the recess cavities 220, 230, 240, 250 using a chemical comprising hydrofluoric acid (HF) or other suitable solution. Then, gaseous and/or liquid precursors may be provided to interact with the composition of the substrate 202 to form the strained material 222, such as silicon germanium (SiGe), to fill the recess cavities 220, 230, 240, 250. In one embodiment, the process for forming the strained material 222 comprising SiGe is performed at a temperature of about 600° to 750° C. and under a pressure of about 10 Torr to about 80 Torr, using reaction gases comprising SiH₂Cl₂, HCl, GeH₄, B₂H₆, H₂, or combinations thereof. In some embodiments, a ratio of a mass flow rate of the SiH₂Cl₂ to a mass flow rate of the HCl is in the range of about 0.45 to 0.55. In one embodiment, the strained material 222 is therefore grown from the facets 230 a, 230 b, 230 c, 230 d, and 230 e to the center of the recess cavity 230 in the substrate 202. In another embodiment, the strained material 222 is therefore grown from the facets 220 a, 220 b, 220 c, and 220 d to the center of the recess cavity 220 in the substrate 202.

In some embodiments, the growth of the strained material 222 in the recess cavity 230 that is not adjacent to the isolation structure 206 a is mainly along the facet 230 c and therefore has an upper surface 222 a formed of (100) crystal plane. In the present embodiment, the growth of the strained material 222 in the recess cavity 220 that is adjacent to the isolation structure 206 a is limited by the isolation structure 206 a because the isolation structure 206 a formed by a dielectric with an amorphous structure fails to offer nucleation sites to grow an epitaxial material. In some embodiments, the growth of the strained material 222 in the recess cavity 220 tends to have an upper surface 222 b formed of (111) crystal plane with a stable surface energy. The strained material 222 in the recess cavity 220 has a lower sidewall surface 222 c formed over the lower sidewall facet 220 b and therefore is formed of (111) crystal plane. In some embodiments, the lower sidewall surface 222 c is parallel to the upper surface 222 b. It can be seen in FIG. 5 that the strained material 222 adjacent to the isolation structure 206 a occupies a small portion of the recess cavity 220.

In FIG. 5A, the semiconductor device 200 is enlarged for better understanding of the profile of the strained material 222 in the recess cavity 220. In the present embodiment, the strained material 222 in the recess cavity 220 has a corner 222 d adjacent to the edge of the gate stack 210 a and having a tip higher than the surface 202 s of the substrate 202. The corner 222 d has a height D3 measured from the surface 202 s to the tip of the corner 222 d. In some embodiments, the height D3 ranges between about 1 nm and about 10 nm.

Referring to FIGS. 1 and 6, the method 100 continues with step 110 in which a cap layer 224 is formed over the strained material 222. In the present embodiment, the cap layer 224 is formed by an epi growth process. In some embodiments, the cap layer 224 functions as a protection layer to prevent undulation of the underlying strained material 222 in a subsequent treatment process. The cap layer 224 over the strained material 222 in the recess cavity 230, which is not adjacent to the isolation structure 206 a, has a thickness D4. In some embodiments, the thickness D4 ranges between about 1 nm and about 5 nm. The cap layer 224 over the strained material 222 in the recess cavity 220 and adjacent to the isolation structure 206 a has a sidewall 224 c contacting the isolation structure 206 a with a thickness D5. In some embodiments, a ratio of the thickness D4 over the thickness D5 ranges between about 1 nm and about 3 nm. In some embodiments, the cap layer 224 over the strained material 222 in the recess cavities 230 may grow along the crystal orientation of the upper surface 222 a and has an upper surface 224 a formed of (100) crystal plane. In some embodiments, the cap layer 224 over the strained material 222 in the recess cavities 220 may grow along the crystal direction of the upper surface 222 b and has an upper surface 224 b formed of (111) crystal plane.

In some embodiments, the cap layer 224 comprises a material different from the strained material 222. In some embodiments, the cap layer 224 is a silicon-containing layer. In the present embodiment, the cap layer 224 is silicon. In some embodiments, the cap layer 224 is formed by a process including selective epitaxy growth (SEG), cyclic deposition and etching (CDE), chemical vapor deposition (CVD) techniques (e.g., vapor-phase epitaxy (VPE) and/or ultra-high vacuum CVD (UHV-CVD)), molecular beam epitaxy (MBE), other suitable epi processes, or combinations thereof. In the present embodiment, the cap layer 224 is formed by a process same as to the process for forming the strained material 222. In some embodiments, the cap layer 224 is continuously formed after forming the strained material 222 by changing the process conditions to be performed at a temperature of about 700° C. to about 800° C., under a pressure of about 10 Torr to about 50 Torr, and using a silicon-containing gas (e.g., SiH₂Cl₂) as reaction gas. In an alternative embodiment, B₂H₆ and/or H₂ are introduced with the silicon-containing gas for forming the cap layer 224.

Referring to FIGS. 1 and 7, the method 100 continues with step 112 in which a treatment is provided to the semiconductor device 200. In some embodiments, the treatment is a heating process. In some embodiments, the treatment is performed at a temperature higher than the temperature for forming the cap layer 224 and/or the temperature for forming the strained material 222. In some embodiments, the treatment is performed at a temperature ranging between about 650° C. to about 850° C. In some embodiments, the treatment is performed under a pressure of about 10 Torr to about 50 Torr and lasting for a period of time not less than about 30 seconds. In some embodiments, a carrier gas (e.g., H₂) with a flow rate of about 35 slm to about 40 slm (standard liters per minute) is introduced in the treatment process for thermal conduction.

After the treatment process, in some embodiments, at least a portion of the corner 222 d of the strained material 222 is redistributed in the recess cavity 220, thereby increasing an amount of the strained material 222 in the recess cavity 220. In one embodiment, the corner 222 d above the surface 202 s of the substrate 202 is completely redistributed in the recess cavity 220, therefore all the strained material 222 is within the recess cavity 220. The increased amount of the strained material 222 in the recess cavity 220 may fabricate a large-volume strained structure to enhance carrier mobility and upgrade the device performance of the semiconductor device 200.

In one embodiment, the redistribution results from reducing the high surface energy of the tip in corner 222 d. In an alternative embodiment, the redistribution is results from a reflow process in the treatment. The original upper surface 222 b of the strained material 222 in the recess cavity 220 is transformed into a treated upper surface 222 b′ after the treatment. In some embodiments, the treated upper surface 222 b′ has a transformed crystal plane which deviates from the original (111) crystal plane, therefore, the lower sidewall surface 222 c of the strained material 222 is not parallel to the treated upper surface 222 b′. In the present embodiment, the treated upper surface 222 b′ has a (311) crystal plane. Accordingly, the upper surface 224 b of the overlying cap layer 224 may be transformed into a treated upper surface 224 b′. In some embodiments, the treated upper surface 224 b′ is transformed from the original (111) crystal plane to the deviated-from (111) crystal plane. In the present embodiment, the treated upper surface 224 b′ has a (311) crystal plane. In some embodiments, the crystal orientation of the upper surface 222 a of the strained material 222 in the recess cavity 230 is not changed after the treatment.

Referring to FIGS. 1 and 8, the method 100 continues with step 114 in which contact features 226 are formed over the cap layer 224. In the present embodiment, the contact features 226 are formed by a process that is the same as the process for forming the strained material 222 or the cap layer 224. The contact features 226 may provide a low contact resistance between the cap layer 224 and a silicide structure formed subsequently. In at least one embodiment, the contact features 226 have a thickness ranging from about 150 Angstroms to about 200 Angstroms. In some embodiments, the contact features 226 comprise a material that is the same as the material of cap layer 224. In alternative embodiments, the contact features 226 comprise a material same as to the material of strain material 222.

It is understood that the semiconductor device 200 may undergo further CMOS processes to form various features such as contacts/vias, interconnect metal layers, dielectric layers, passivation layers, etc. In some embodiments, the gate stacks 210 a, 210 b, 210 c may be dummy gate stacks. Thus, the CMOS processes further comprise a “gate last” process to replace the polysilicon gate electrode with a metal gate electrode to improve device performance. In one embodiment, the metal gate electrode may include a metal such as Al, Cu, W, Ti, Ta, TiN, TiAl, TiAlN, TaN, NiSi, CoSi, other suitable conductive materials, or combinations thereof. It has been observed that the modified strained structure provides a given amount of strain into the channel region of a semiconductor device, thereby enhancing the device performance.

The various embodiments of the present disclosure discussed above offer advantages over previously known methods, it being understood that no particular advantage is required for all embodiments, and that different embodiments may offer different advantages. One of the advantages is that the lower portion of the strained material in the S/D recess cavity adjacent to the isolation structure may be increased to enhance carrier mobility and upgrade the device performance. Another advantage is that the likelihood of device instability and/or device failure resulting from forming a subsequent silicide over the lower portion of the strained material may be prevented.

In one embodiment, a semiconductor device includes a gate stack, an isolation structure and a strained feature. The gate stack is over a substrate. The isolation structure is in the substrate. The strained feature is disposed between the gate stack and the isolation structure and disposed in the substrate. The strained feature includes an upper surface adjacent to the isolation structure having a first crystal plane and a sidewall surface adjacent to the gate stack having a second crystal plane. The first crystal plane is different from the second crystal plane.

In another embodiment, an integrated circuit includes a gate, an isolation structure, a strained feature and a cap layer. The gate is over a substrate. The isolation structure is in the substrate. The strained feature is disposed between the gate and the isolation structure and disposed in a wedge-shaped recess cavity in the substrate. The strained feature includes an upper surface not parallel to a top surface of the substrate.

In still another embodiment, a semiconductor device includes a first gate and a second gate, an isolation structure, a first strained feature and a second strained feature. The first gate and the second gate are over a substrate. The isolation structure is in the substrate. The first strained feature is disposed between the first gate and the isolation structure and disposed in the substrate. The first strained feature includes a first upper surface having a first crystal plane. The second strained feature is disposed between the first gate and the second gate and disposed in the substrate. The second strained feature includes a second upper surface having a second crystal plane. The first crystal plane is different than the second crystal plane.

While the disclosure has described by way of example and in terms of the preferred embodiments, it is to be understood that the disclosure is not limited to the disclosed embodiments. To the contrary, it is intended to cover various modifications and similar arrangements (as would be apparent to those skilled in the art). Therefore, the scope of the appended claims should be accorded the broadest interpretation so as to encompass all such modifications and similar arrangements. 

What is claimed is:
 1. A semiconductor device, comprising: a gate stack over a substrate; an isolation structure in the substrate; and a strained feature disposed between the gate stack and the isolation structure and disposed in the substrate, wherein the strained feature comprises: an upper surface adjacent to the isolation structure having a first crystal plane; and a sidewall surface adjacent to the gate stack having a second crystal plane, wherein the first crystal plane is different from the second crystal plane.
 2. The device of claim 1, further comprising: a contact feature over the strained feature.
 3. The device of claim 2, further comprising: a cap layer between the strained feature and the contact feature.
 4. The device of claim 1, wherein the first crystal plane is (311).
 5. The device of claim 1, wherein the second crystal plane is (111).
 6. The device of claim 1, further comprising: an epi Si layer over the strained feature.
 7. The device of claim 1, wherein a top surface of the substrate is disposed above the upper surface of the strained feature.
 8. The device of claim 1, wherein the sidewall surface of the strained feature is not parallel with the upper surface of the strained feature.
 9. An integrated circuit, comprising: a gate over a substrate; an isolation structure in the substrate; a strained feature disposed between the gate and the isolation structure and disposed in a wedge-shaped recess cavity in the substrate, wherein the strained feature comprises an uppermost surface not parallel to a top surface of the substrate; and a cap layer over the strained feature.
 10. The integrated circuit of claim 9, wherein the uppermost surface has a first crystal plane, and wherein the strained feature further comprises: a sidewall surface adjacent to the gate having a second crystal plane, wherein the first crystal plane is different from the second crystal plane.
 11. The integrated circuit of claim 10, wherein the sidewall surface of the strained feature is not parallel with the uppermost surface of the strained feature.
 12. The integrated circuit of claim 11, wherein the first crystal plane is (311) and the second crystal plane is (111).
 13. The integrated circuit of claim 9, wherein a top surface of the substrate is disposed above or equal to the uppermost surface of the strained feature.
 14. The integrated circuit of claim 9, wherein the cap layer is disposed in the wedge-shaped recess cavity in the substrate.
 15. The integrated circuit of claim 9, further comprising a contact feature over the strained feature.
 16. A semiconductor device, comprising: a first gate stack over a substrate; an isolation structure in the substrate; a first strained feature between the first gate stack and the isolation structure and disposed in a recess cavity in the substrate, wherein the first strained feature comprises: an upper surface adjacent to the isolation structure having a first crystal plane, wherein the upper surface is angled with respect to a top surface of the substrate; and a sidewall surface adjacent to the first gate stack having a second crystal plane, wherein the first crystal plane is different from the second crystal plane; and a cap layer over the first strained feature.
 17. The semiconductor device of claim 16, further comprising: a second gate stack over the substrate; and a second strained feature between the first gate stack and the second gate stack and in the substrate, wherein the second strained feature comprises an upper surface having a third crystal plane, wherein the first crystal plane is different than the third crystal plane.
 18. The semiconductor device of claim 17, wherein the first crystal plane is (311) or (111) and the third crystal plane is (100).
 19. The semiconductor device of claim 16, wherein the top surface of the substrate is above the upper surface of the first strained feature.
 20. The integrated circuit of claim 9, wherein a surface of the cap layer is planar. 